Aim: This study aims to measure the amount of fluoride release in deionized water from two composite resins materials (Kerr and Tetric ceram)over period of one month. By using different curing time for curing the composite.Materials and Methods : Two types of composite resin materials were used.
They are Tetric ceram and Kerr composite resins divided into five groups for each type of materials used, each group contain ten sample materials and cured with different time of curing which are (20,30,40,50,60) seconds.The samples measured fluoride release after storing in 5ml of deionized water then incubated incubator at 37°C for 24 hours.Results: The amount of fluoride release was affected by the period of curing time. The materials which cured at (20,30,40) seconds gave high amount of fluoride release while the materials which cured at (50,60)seconds gave low amount of fluoride release.
Conclusions: The amount of fluoride release from composite resins materials were affected by curing time. There is an increase in the amount of fluoride release by decreasing the period of curing time and decreasing by increasing the period of curing time.
Inhaltsverzeichnis (Table of Contents)
- ABSTRACT
- INTRODUCTION
- MATERIALS AND METHODS
- RESULTS
- DISCUSSION
- CONCLUSION
- REFERENCES
Zielsetzung und Themenschwerpunkte (Objectives and Key Themes)
This study investigates the impact of curing time on fluoride release from two composite resin materials: Kerr and Tetric ceram. The primary goal is to measure the amount of fluoride released into deionized water over a period of one month, examining the effects of varying curing times.
- Fluoride release from composite resin materials
- Influence of curing time on fluoride release
- Comparison of fluoride release between different composite resin brands
- Degree of conversion of the composite resin matrix
- Cariostatic effect of fluoride
Zusammenfassung der Kapitel (Chapter Summaries)
- ABSTRACT: This chapter summarizes the study's aims, materials, methods, results, and conclusions. It highlights the influence of curing time on fluoride release from composite resin materials.
- INTRODUCTION: This chapter introduces the role of fluoride as a cariostatic agent and discusses the importance of fluoride release from restorative materials. It emphasizes the properties of composite resins and their use in modern dentistry.
- MATERIALS AND METHODS: This chapter details the materials and methods used in the study. It explains the preparation of composite resin samples, curing procedures, fluoride release measurement techniques, and the use of a standard solutions curve.
- RESULTS: This chapter presents the results of the study, showing the fluoride release levels for both Tetric ceram and Kerr composite resins at different curing times. It includes statistical analysis using ANOVA to determine the significance of the differences between groups.
- DISCUSSION: This chapter analyzes the results and interprets their significance. It discusses the mechanisms of fluoride release from composite resins, the role of curing time in affecting the degree of conversion, and the implications of the findings for clinical practice.
Schlüsselwörter (Keywords)
The study focuses on the key concepts of curing time, fluoride release, composite resin, and cariostatic effect. The research investigates the relationship between the curing time of composite resins and the amount of fluoride released, examining the potential impact on dental health and caries prevention.
- Arbeit zitieren
- Amer Taqa (Autor:in), Manal A. Sultan (Autor:in), 2008, The Effect of Curing Time on Fluoride, München, GRIN Verlag, https://www.grin.com/document/209001